17-4 Precipitation Hardening also known as Type 630 is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and a moderate level of corrosion resistance. High strength is maintained to approximately 600 degrees Fahrenheit (316 degrees Celsius). Alloy 17-4 PH is a precipitation hardening
ASTM-A564 Grade 630 UNS S17400 JIS SUS630 AMS 5643 5604 EN10088-3 H900 H1025 H1075 H1150D. Alternative stainless grades we supply. FV520B S31254 904L 310 321 316 440B 440C 420 410 416 431 S31803 S32760 17-4PH, H1150D, ASTM A564, Double : Translate this pageDec 01, 2020 · H1150 Heat treatment 1150 . H1150D Double . 1150 . H1150 + H1150 . 17-4PH 17-4 Chromium 17%. Nickel 4% ,Cu 4% . 17
Translate this pageMay 26, 2016 · ASTM A564 Type 630. SUS630 . , . . . 17-4PH (630), 17-7 (631) . , ASTM AMS 5936 ASTM A564 / A693 / F899 Medical Steel for Properties of medical steel Custom 465 / AMS 5936 / ASTM A564 / A693. Utilized as a premium steel of the newest generation, Chronifer 465 KL was conceived to eliminate the setbacks that were encountered with steel used for medical instrumentation namely corrosion, tensility and breakage. This superior melted martensitic, age hardenable steel is designed for use in applications in fields that require excellent
17-4PH datasheet, AISI 630 Chemical, AISI 630 mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specification - ASTM A564. ASTM A564 Specification 17-4PH Stainless Steel Aero-VacStainless Steel Rings. 16 Cr, 4.0 Ni, 0.30 Cb Ta, 4.0 Cu. 17-4PH Stainless Steel in ASTM A564 Specification, per ASTM International:This specification covers bars and shapes of age-hardening stainless steels. Hot-finished or cold-finished rounds, squares, hexagons, bar shapes, angles, tees, and channels are included.
ASTM A564 is a standard material specification for hot-rolled and cold-finished age-hardening stainless steel bars, including type 630 / UNS S17400 / 17-4 PH used for parts requiring corrosion resistance and high strength at room temperature, or at temperatures up to 600°F [315°C]. Boltport uses S17400 round bars to ASTM this specification to manufacturer bolts, screws, studs, rods and custom bolting. Encore Metals - 17-4PH, T-63017-4PH, T-630. 17-4PH offers a unique combination of properties:high strength, excellent corrosion resistance, good fatigue strength, superior resistance to galling and seizing, easily heat treated by a short, simple low temperature treatment with minimal distortion and no scaling. Parts may be finish-machined before hardening.
kg] Type 630, Solution,Annealed Cold Finished Ccnterlcss Ground, 1 in. .0 mm] round bar. 10 to 12ft [3.0 to 3.6 m] in length, ASTM A 564 dated . End usc:valve shafts. 4. General Requirements 4.1 In addition to the requirements of this specification, all requirements of the current edition of Specifications A 484/ A 484M shall apply. Sorry, we have detected unusual traffic from your network.Sorry, we have detected unusual traffic from your network. Please slide to verify help help
Alloy 17-4PH (UNS S17400), Type 630, is a chromium-nickel-copper precipitation-hardening martensitic stainless steel with an addition of niobium. 17-4PH combines high strength and hardness with good corrosion resistance. The alloy is furnished in the solution annealed condition (Condition A). It Speedy Metals Information for 17-4 PH Condition A17-4 stainless generally conforms to ASTM A564 Type 630 AMS 5643. MECHANICAL PROPERTIES. The above values are average and may be considered as representative of 17-4 stainless. Condition H1150°- 1150° F for 4 hours, air cool. Rockwell C 33 average Annealing (Condition A)
- Chemical FormulaIntroductionKey PropertiesCompositionMechanical PropertiesPhysical PropertiesGrade Specification ComparisonPossible Alternative GradesCorrosion ResistanceHeat ResistanceFe, <0.07% C, 15-17.5% Cr, 3.0-5.0% Ni, <1.0% Mn, <1% Si, <0.040% P, <0.03% S, 3.0-5.0% Cu, 0.15-0.45% Nb+TaAms 5643 Astm A564 Type 630 Steel Bar Suppliers Mumbai Astm A564 Uns S17400 Round Bar, Astm A564 Jis Flat Bars, Astm A564 Sus630 Square Bar, Astm A564 Tp630 Supplier Astm A564 Steel Rod, Astm A564 Type 630 Box Bar, SS Astm A564, Astm A564 Ams 5643 Stockist & Suppliers in India, South Africa, Indonesia, Dubai, Brazil, Sri
Stainless Steel 17-4PH Bar (AMS 5643 / AMS 5622 ASTM A 693 Plate, Sheet and Strip UNS :S17400 17-4 DBLE H1150 ASTM A 564 T 630 Cond H1150D NACE MRO175/ISO 15156-3. 17-4 PH Cond H 1150 ASTM A 564. 17-4 PH Sol AMS 5643 ASTM A 484 AMS 5604 Sheet, Strip Cold Rolled and Plate. AMS 5622 (Vac Melt) Bars (Flat, Hex, Round, Square), Wire, Forgings, Tubing and Rings AMS 5642 Bar
3.0 - 5.0. 17-4 PH is a martensitic, precipitation-hardening stainless steel that provides an outstanding combination of high strength and hardness along with excellent corrosion resistance. 17-4 PH has good fabricating characteristics and can be age hardened by a single step, low temperature treatment. 17-4 PH is a versatile material widely Stainless Steel AL 17-4 PrecipitationAlloy (S17400), Type 630, is a chromium-nickel-copper precipitation hardening stainless steel used for applica-tions requiring high strength and a moderate level of corrosion resistance. High strength is maintained to ap-proximately 600°F (316°C). The S17400 alloy is martensitic in structure in the an-
630 (17-4ph) Heat Treatment To ASTM A564/A564M and EN10088-3 After annealing from 1030°C to 1050°C, 1.4542 presents a soft martensitic structure with a hardness of around 35 HRC.A564 Type 630 Condition H1150 ferritic or austenitic Jun 13, 2008 · 13 Jun 08 16:37. Hey Everyone, I am using a stainless steel bolting material which is designated ASTM A564 Type 630, Condition H1150. I am qualifying it using the ASME BPV Code (Section III, Subsection NF) which has different allowables for ferritic and austenitic materials but I can't seem to find guidance for martensitic materials.